Product Details:
Payment & Shipping Terms:
|
| Application: | Industry Furnace Heating Element | Shape: | Strip,ribbon, Flat Wire |
|---|---|---|---|
| Material: | FeCrAl,Iron-Chromium-Aluminium Alloy | Chemical Composition: | Fe Cr Al,Ferro Chrome Aluminium |
| Dimensions: | As Client's Requirement | Surface: | Acid White/oxidized |
| Density: | 7.9g/cm3 | Color: | Acid White Or Oxidized |
| Standard: | GB/1234 2012 | Melting Point: | 1500℃,1450℃ |
| Feature: | Good Form Stability | Resistivity: | 1.45±0.06 |
| Product Name: | Alloy Electric Heating Element | Size: | As Your Required |
| High Light: | nichrome wire,nichrome resistance wire,nickel chromium resistance wire |
||
FeCrAl heating element / heating strip for Industrial Furnace
Product Description:
Our company mainly produces high-temperature heating strip with low impurities, high purity, good surface oxidation resistance, stable resistivity, corrosion resistance, good processing performance and high temperature strength and weldability. The products can be directly processed into winding, Z-shaped, spiral, etc., and widely used in metal smelting, mechanical manufacturing, industrial electric furnaces, small electric furnaces, muffle furnaces, household appliances, transportation and other industries to produce heating elements and resistance components. Our product specifications are complete in advanced technology and guaranteed quality. Welcome new and old customers to order!
The advantages of high temperature heating strip:
Our product has a long service life and high temperature resistance, such as the maximum service temperature of HRE iron-chromium aluminium alloy wire can reach 1400℃in the atmosphere; the oxidation resistance of the product surface is very good, the AI2O3 film formed after oxidation has a good high resistivity and resistance; and the allowable surface load is large; its specific gravity is smaller than that of nickel-chromium alloy; its resistivity is also higher and the sulfur resistance is better; but Its price is obviously lower than that of nickel-chromium alloy.
| Material |
OHM |
0Cr21Al6Nb | 0Cr25Al5 | 0Cr23Al5 | 0Cr19Al5 | 0Cr19Al3 | 1Cr13Al4 | Cr20Ni80 | Cr15Ni60 | |
|
Nominal composition |
Cr | 24 | 21 | 25 | 23 | 19 | 19 | 13 | 20 | 15 |
| Al | 6 | 6 | 5.3 | 5 | 5 | 3 | 4 | / | / | |
| Fe | Bal | Bal | Bal | Bal | Bal | Bal | Bal | / | 25/ | |
| Ni | / | / | / | / | / | / | / | Bal | Bal | |
|
Max |
1400 | 1350 | 1300 | 1250 | 1200 | 1100 | 950 | 1200 | 1150 | |
| Resistivity(μΩ.m) | 1.45 | 1.43 | 1.4 | 1.35 | 1.33 | 1.23 | 1.25 | 1.09 | 1.11 | |
|
Temperature factor |
800℃ | 1.03 | 1.03 | 1.05 | 1.06 | 1.05 | 1.17 | 1.13 | 1.04 | 1.1 |
| 1000℃ | 1.04 | 1.04 | 1.06 | 1.07 | 1.06 | 1.19 | 1.14 | 1.05 | 1.11 | |
| 1200℃ | 1.04 | 1.04 | 1.06 | 1.08 | 1.06 | / | / | 1.07 | 1.13 | |
| Denstiy(g/cm3) | 7.1 | 7.1 | 7.15 | 7.25 | 7.2 | 7.35 | 7.4 | 8.3 | 8.2 | |
| Melting temp(℃) | 1500 | 1500 | 1500 | 1500 | 1500 | 1500 | 1450 | 1400 | 1400 | |
| Elongation(%) | 16 | 16 | 16 | 16 | 16 | 16 | 16 | 25 | 25 | |
| Magnetic properties | Yes | Yes | Yes | Yes | Yes | Yes | Yes | Yes | Yes | |