Product Details:
Payment & Shipping Terms:
|
Chemical Composition: | 21%Cr 6%Al Balance Fe And Nb | Dimensions: | 0.02-10mm |
---|---|---|---|
Material: | Alloy | Shape: | Wire |
Application: | Industry And Household Appliances | Resistivity(μΩ.m): | 1.45 |
Tensile Strength (≥ MPa): | 720 | Elongation (≥ %): | 20 |
Yield Strength (≥ MPa): | 520 | Density (g/cm3): | 7.16 |
Working Temperature(℃): | 1250 | OEM: | Available |
Annealing Treatment: | Hydrogen Annealing | Surface Treatment: | Bright Oxidation |
Certificate: | SGS, IOS | ||
High Light: | heating wire,high temp alloys |
Household Appliances FeCrAl Alloy Resistance Strip Hydrogen Annealing Wire Shape
OHMPM145 Strip
(Common name: Kanthal APM)
Ohmalloy Material Co., Ltd. has long been committed to research and development of electrothermal alloy products with good oxidation resistance and high temperature resistance. OHMPM145 alloy is a new product developed after HRE alloy which has been widely used in high temperature electrothermal alloy materials in recent years. Compared with HRE, its purity and oxidation resistance is further improved and optimized. With special rare earth elements and unique metallurgical manufacturing process, OHMPM145 has been recognized by customers in the field of high temperature heat-resistant fibers around the world. It has been successfully applied in ceramic sintering, diffusion furnace, high power density and high temperature industrial kiln.
Grade and Chemical Composition
Grade | Chemical composition% | ||||
C | Si | Cr | Al | Fe | |
OHMPM145 | ≤0.04 | ≤0.4 | 20-23 | 5.8 | Bal. |
Specification
Type: | Dia(mm) | Thickness(mm) | Width(mm) |
Round wire: | φ0.15-8.0 | - | - |
Flat wire: | - | 0.1-0.4 | 0.5-4.5 |
Strip: | - | 0.5-2.5 | 5-48 |
Performance and Application
Grade | OHMPM145 |
Max.operating temperature | 1425ºC |
Tensile Strength (N/mm2) | 650-800 |
Elongation% | >14 |
Resistivity at 20ºC | 1.45 |
Application | High Temperature Ceramic Firing Furnace/High Temperature Heat Treatment Furnace/High Temperature Diffusion Furnace in Electronic Industry |
Average linear expansion coefficient
TemperatureºC | 20-250 | 20-500 | 20-750 | 20-1000 | 20-1200 | 20-1400 |
Thermal expansion coefficient×10-6/k | 11 | 12 | 14 | 15 | - | - |
Thermal Conductivity
50ºC 600ºC 800ºC 1000ºC 1200ºC 1400ºC
Wm-1k-1 11 20 22 26 27 35
Resistance Temperature Coefficient
Temperature(ºC) 700 900 1100 1200 1300
Ct 1.02 1.03 1.04 1.04 1.04