Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core

Certification
Good quality Bimetallic Strip for sales
Good quality Bimetallic Strip for sales
I search for Nichrome plate long time, and successfully bought it from Ohmalloy material. OHMALLOY provide real good service in alloy service and can always help me in finding the correct resistance alloy.

—— Mike Harness

OHMALLOY can provie me only 1kg Kovar alloy wire 1.0mm with short time, that is really amazing. Thanks

—— Janey

Really professional in thermocouple wire and cable, what i want just can get from OHMALLOY

—— Chris

Enamelled Constantan 0.08mm, i never expect to get only 2kg of it. But OHMALLOY supply it to me with good quality. God Jesus! Such a reliable supplier from china

—— Aaron

I'm Online Chat Now

Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core

China Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core supplier
Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core supplier Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core supplier Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core supplier Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core supplier Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core supplier Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core supplier

Large Image :  Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core

Product Details:

Place of Origin: jiangshu
Brand Name: Ohmalloy/OEM
Certification: SGS
Model Number: SP-1K107

Payment & Shipping Terms:

Minimum Order Quantity: 30 piece
Price: USD 0.98/Piece
Packaging Details: Coil,paper wrapped,carton outside
Delivery Time: 5-8 working days after payment confirmed
Payment Terms: L/C, T/T, Western Union, MoneyGram,paypal
Supply Ability: 50Tons per month
Contact Now
Detailed Product Description
Name: Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core Usage: Transformer Inductor Iron Amorphous Core
Size: 10-50mm(Customized) State: Strip/ Ribbon/Curing

Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core

Nanocrystalline Core Strip Ribbon 1K107 Transformer Inductor Iron Amorphous Core

 

Application area:

Switch power transformer and Pulse transformer iron core

Power transformer , precision current mutual inductor iron core

Leakage protection switch mutual inductor iron core

Filtering inductance, storage inductance, the electric reactor iron core

EMC common mode inductance and differential mode inductance iron core

Saturable reactor, magnetic amplifier, Spike killer, Pulse Compressor iron core and magnetic bead

Features:

High Saturation magnetic induction - reduce transformer volume

High magnetic permeability low coercive force- improve transformer efficiency, mutual inductor sensitivity, reduce coil distribution parameters

Low loss- reduce transformer temperature rise

Good temperature stability - under 130℃ for long-term work

Lower price - has the best cost performance of all the metal soft magnetic material

Typical Properties

Physical properties of Nanocrystalline alloy

 

Saturation magnetic induction (Bs) 1.25T Hardness (Hv) 880
Curie temperature (TC) 560℃ Density (d) 7.2g/cm3
Crystallizing temperature( Tx) 510℃ Resistivity(r) 90mW-cm
Saturation magnetostriction coefficient (ls) <2×10-6 Continuous operating temperature range -55-130℃

Magnetic properties of Nanocrystalline alloy

Product Type Transverse magnetic annealing No magnetic annealing Longitudinal magnetic annealing
Initial permeability >2×104 >8×104 >1×104
Maximum permeability >5×104 >45×104 >50×104
Residual magnetic induction <0.2 T 0.6 T >0.85 T
Coercive force <1.8A/m <0.8A/m <1.8A/m
Iron loss P(20kHz, 0.5T) <30W/kg <50 W/kg <90W/kg
Iron loss P(100kHz, 0.3T) <150W/kg <150 W/kg <300W/kg
Iron loss rate(-55°C –125C ) <15% <15% <15%

The comparison between Nanocrystalline alloy and Permalloy iron alloy

Basic parameter Superfine crystal iron core Permalloy iron alloy (1J85) Ferrite
Saturation magnetic induction Bs(T) 1.25 0.75 0.5
Residual magnetic induction Br(T) 0.2~0.9 - 0.20
Saturation magnetostriction coefficient (×10-6) <2 <2 4
Resistivity (mmW-cm ) 80 56 106
Curie temperature / 570 400 <200
Initial permeability μ0(Gs/Oe) >8×104 >8×104 -
Maximum permeability μm(Gs/Oe) >50×104 60×104 4×104
Coercive force Hc (A/m) <2 <1 6
Iron loss (20KHz,0.5T) (W/Kg) <35 - No
Iron loss (50KHz,0.3T) (W/Kg) <50 - No